Corrosion Blamed in Fatal Plant Blast

Monday, November 18, 2013

More items for Health & Safety

Comment | More

Stress corrosion cracking and a lack of inspections likely caused the fatal explosion at an Illinois manufacturing plant in 2009, the U.S. Chemical Safety Board has concluded.

One person 650 feet away was killed and one was injured in the blast, which originated in a vessel growing synthetic quartz at extremely high temperatures and pressures for Nihon Dempa Kogyo (NDK) Co. Ltd., in Belvidere, IL.

The company produces and sells crystal-related products used in cell phones and wireless Internet devices.

'Falling Through the Cracks'

The CSB published its draft investigation report Thursday (Nov. 14) in the form of a Case Study. The board also released a video, Falling Through the Cracks, which uses computer animation to show the accident's sequence of events and findings of the investigation.

During the explosion Dec. 7, 2009, a piece of steel was blown off the building, striking and killing a driver who was walking back to his car at a gas station 650 feet away

A vessel fragment weighing more than 8,000 pounds blew through the facility's wall, crossed over a parking lot, and struck the wall of an automotive supply company where 70 people were working, injuring one.

No NDK employees were injured.

NDK Crystal company explosion
Photos and video: U.S. Chemical Safety Board

The CSB says stress corrosion cracking likely caused a vessel at this Belvidere, IL, crystal manufacturing plant to explode in 2009, sending shrapnel hundreds of feet in several directions. One person was killed and one was injured.

NDK immediately shut down all operations at the plant and has not resumed them. The Illinois facility was Japan-based NDK's only U.S. production site.

Direct Warnings Ignored

In NDK's vessels, raw mined quartz, or silica, was mixed with corrosive sodium hydroxide solution at high pressures and temperatures. This resulted in a reaction with the steel vessels that formed a layer of iron silicate, called acmite, on the inside of the vessel walls, which the company believed would protect the vessels from corrosion.

Despite warnings that corrosion might still be occurring under the acmite, NDK kept operating the vessels without performing inspections, the Chemical Safety Board report says.

"After a review of the metallurgical testing data, the CSB found strong evidence of cracking on and near the inner diameter of the vessel fragment," Johnnie Banks, CSB lead investigator, said in a press release. "The cracks reduced the vessel material toughness, which eventually led to large flaws, resulting in the catastrophic failure.

"Stress corrosion cracking was the likely failure mechanism that caused the cracks. Had NDK conducted regular inspections, it would have discovered that the acmite coating was not protecting the vessel walls," said Banks.

The CSB's Falling Through the Cracks uses animation to show the events leading up to the explosion.

Temper embrittlement, or another form of heat treatment embrittlement, may have been a contributing factor in addition to the stress corrosion cracking, the report says.

The board also found that the company ignored a direct warning from a third-party safety auditor sent by its insurance carrier after a hot, caustic material leaked from the lid of a similar pressure vessel in January 2007.

The auditor said the leak had stemmed from the vessel's improper design, fabrication and material selection. He said that four vessels at the facility were showing stress corrosion cracking and advised against returning any of the facility's eight vessels to service.

The auditor said "far more catastrophic scenarios are possible" and specifically warned of public death or injury at the gas station where the truck driver was later killed, the CSB found.

However, NDK neither established an internal vessel inspection program nor tested the vessels before returning them to service.

'Near-Inevitable Catastrophe'

"Over the years, NDK ignored safety recommendations and warnings that it should regularly inspect the interior walls of the vessels," CSB Chairperson Rafael Moure-Eraso said.

In addition, the Illinois Board of Boiler and Pressure Vessel Safety incorrectly designated the vessels for non-corrosive service and did not conduct internal inspections, the CSB said. In 2003, in 2006, and three months before the 2009 explosion, the state conducted three inspections of the vessel that later failed, but it focused only on accessible external surfaces.

CSB explosion report

A safety auditor from NDK's insurance company specifically warned about the possibility of death or injury at the gas station where a truck driver was killed during the explosion.

"Because the vessels did not meet the requirements of the widely recognized national pressure vessel code, the State of Illinois allowed installation of three of the vessels under a special exemption. In doing so, the vessels were incorrectly put into 'non-corrosive' service.

"The manufacturer of the vessels—including the one that exploded years later—recommended annual inspections, but neither NDK nor the state performed the inspections. This set in motion a near-inevitable catastrophe," Moure-Eraso said.

Nor did the vessels meet American Society of Mechanical Engineers standards, the report found. NDK's vessel walls were eight inches thick, while the recommended limit is seven inches, making them possibly too thick for proper heat treatment during manufacturing, according to the CSB.

Zoning Questions

The CSB also examined the laws that allowed NDK to be built near the Illinois Tollway gas station and other nearby businesses, discovering that the property was zoned "light industrial" when it should have been considered "heavy industrial."

"NDK was not identified as a potential risk to the nearby community when it was built in 2001," Moure-Eraso said. "In this and other CSB investigations, we express concern that potentially hazardous chemical facilities are permitted to be built near, or to continue to operate near public facilities.

"Particularly where the public might be endangered, companies should pay all the more attention to near misses and other warnings to preclude catastrophic accidents."

   

Tagged categories: Accidents; Corrosion; Cracking; Explosions; Fatalities; Tanks and vessels; U.S. Chemical Safety Board

Comment Join the Conversation:

Sign in to our community to add your comments.

Bullard

The Next Generation
of Blasting

• Lightest
• Coolest
• Most Comfortable
• Most Dependable


Clemco Industries Corp.
Powerful Protection in a Small Package

Mounts inside blast helmet, alerts operator to dangerous breathing-air condition by audible, visual, and vibratory alarms. Easily calibrated, battery operated.


ABKaelin, LLC
Quality is our bottom line

Services include:
• Environmental, Health &
  Safety
• Contractor QP Certification
• Quality Assurance Programs
  and Auditing
• SSPC C3/C5 and other
  Training
• Coatings
• Design/Construction
See our website at abkaelin.com or contact us today abkaelin@comcast.com


U.S. Zinc

The proven corrosion protection properties of our zinc dust prolong the life of marine coatings. U.S. Zinc – Helping the world work™


Modern Safety Techniques
Modern Safety Techniques

See our Low Temperature Catalyst for your CO removal needs. Help to provide your workers with safe, comfortable breathing air!


Mitsubishi Gas Chemical America
Performance Amine 1,3-BAC

A highly reactive cycloaliphatic diamine offering superior performance. Reasonable cost and curing efficacy makes it suitable for all types of epoxy resin applications.


Termarust Technologies
Termarust (HR CSA) Chemically Stops
Active Corrosion

Truss bridge treated with Termarust's (HR CSA) in 1995. This highway & rail truss bridge is still stable and there still is no active corrosion.

 
 
 
Technology Publishing

The Technology Publishing Network

The Journal of Protective Coatings & Linings (JPCL) PaintSquare
Durability + Design Paint BidTracker JPCL Europe

 
EXPLORE:      JPCL   |   PaintSquare News   |   Interact   |   Buying Guides   |   Webinars   |   Resources   |   Classifieds
REGISTER AND SUBSCRIBE:      Free PaintSquare Registration   |   Subscribe to JPCL   |   Subscribe to PaintSquare News
MORE:      About PaintSquare.com   |   Privacy policy   |   Terms & conditions   |   Site Map   |   Search   |   Contact Us
 

© Copyright 2000-2014, Technology Publishing / PaintSquare, All rights reserved
2100 Wharton Street, Suite 310, Pittsburgh PA 15203-1951; Tel 1-412-431-8300; Fax 1-412-431-5428; E-mail webmaster@paintsquare.com